Here are some thoughts about the options.
Laminex/Formica
Probably the most popular benchtop available in a wide range of colours and patterns and reasonably hardwearing.
Just don’t get one with a textured finish.
We made that mistake once, never again.
Tiles
Wide range of colours and sizes, a few problems are;
-
-
-
- Uneven surface
- Dealing with the exposed tile edges,
- Keeping the grouted joints clean.
-
-
Wood
Can look good but will tend to suffer chips and dents.
Can stain easily especially around the sink.
Requires a lot of maintenance to keep its looks.
Marble
A natural stone which can look very attractive.
For kitchen benchtops its big problem is that it is porous and not very acid resistance.
Any breakdown of the surface sealant will result in staining which is nearly impossible to remove.
Granite
Available in a wide range of Colours including light greys.
Being less porous than marble staining is less of a problem.
Matching can be a problem if a piece is damaged during installation so its best installed by professionals to get the jointing right.
Engineered Stone
This covers a wide range of materials.
Basically it is consists of natural stone chips, which are mixed with some binding agent to form a stone like surface.
The binder can be anything from cement, to polymers, and epoxy resins.
Very resistant to stains and is available in a wide range of colours and can usually be easily matched.
Very durable, but usually more expensive than a natural stone like granite.
Keep away from the installation as the dust can cause major health problems.
Stainless Steel
The standard choice for commercial kitchens because its easy to clean.
Currently more of a fashion statement, which isn’t for everybody.
Will probably look dated as another look replaces the commercial look.
One issue I have found with the stone type products is that they are much noisier when you put plates down.
Not too good for me as the kitchen is next to the bedroom, and I get up over an hour before my wife.
Finally
On cost I would choose laminex but for a more classy look it would be either granite or one of the engineered stones.
Before you make a decision remember that you shouldn’t cut food directly on a benchtop.
Always cut it on either a wooden or plastic cutting board, other wise you will damage your knives and/or the benchtop.
There’s also the acrylic ones to consider !
Good Point. I tend to think of them as similar to engineered stone.
Brian
We’re shopping for our new house now and have found the choices to be ………..
1) Laminex (or equivalent) …Can be cheapest, vast array of colours / styles, been around for a zillion years, you parents probably had it in the house you grew up in !
2) Natural stones ……Marble too soft, so quartz / granite. Probably most heat resistant, “limited” range of colours / sizes, can stain, needs to be resealed.
3) Acrylic…..A good option, can be made to any size with invisible joins, can be repaired / repolished if damaged, question as to heat durability.
4) Engineered stone…Possibly the best “all-round” compromise
Thanks for the opinions its always interesting to see what others think.
Brian